Different Size Aluminium Industrial Profiles Radiator Profile With Polishing
Detailed Product Description
|
Product Name:
|
Aluminium Heat Sink
|
Alloy:
|
6063
|
|
Material :
|
Aluminium Alloy
|
Surface Treatment:
|
Polishing
|
|
Deep Process :
|
Milling,Cutting
|
Length:
|
Customized
|
Different Size Aluminium Industrial Profiles Radiator Profile With Polishing
About us :
Deyuan Metal Foshan Co., Ltd. is a comprehensive and professional enterprise integrating research, design production and sales of aluminium extrusion profiles for construction and industrial applications. There are currently 26 aluminum extrusion process lines at 500MT TO 2500MT, 3 process lines for anodizing, 2 process lines for powder coating, 1 process line for painting, 1 process line of polishing and brushing. Our annual production capacity has reached 80,000 tons which is at the forefront of the aluminium industry in China.
Description:
| Material |
6063 |
| Surface |
Mill Finished, |
| Color |
Natural |
| MOQ |
1ton. Usually 12 tons for a 20 feet container; 24 tons for a 40 feet container. |
| Length |
For Anodizing and Electrophoresis: Maximum 6.8 Meters
For Powder Coating : Maximum 12 Meters
|
| Packing |
1) EPE, waterproof paper wrapped in small bundles.
2) paper interleave each piece and packing in wooden box and finally on Steel Rack to pull into container |
| Sample delivery |
Two weeks (one week for mould +one week making sample) |
| Sample design |
It is better we can get your drawing or sample, we mainly make according to your design, and we can keep confidential for your design. |
| Maximum extruder machine |
3500 tons; Minimum extruder machine: 500 tons |
Equipment:
| Production lines |
Quantity |
Max product length |
| Extrusion press |
26 press range from 500MT to 2500MT |
Circumcircle diameter≤2200mm |
| Anodizing and electrophoresis |
3 |
≤7500mm |
| Powder Coating |
2 |
≤8500mm |
| Wood Grain |
1 |
≤8500mm |
| Painting |
1 |
≤8500mm |
| Polishing |
1 |
≤6000mm |
| Brushing |
1 |
≤6000mm |
Primary Technical Data
1) Chemical composition
| Alloy |
Si |
Mg |
Fe |
Cu |
Mn |
Zn |
Cr |
Ti |
| 6063 |
0.2~0.6 |
0.45~0.90 |
<0.35 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
| 6060 |
0.3~0.6 |
0.35~0.60 |
0.1~0.3 |
~ |
<0.10 |
<0.15 |
<0.05 |
~ |
| 6463 |
0.2~0.6 |
0.45~0.90 |
<0.15 |
<0.20 |
<0.05 |
<0.05 |
~ |
~ |
| 6005 |
0.6~0.9 |
0.40~0.60 |
<0.35 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
| 6061 |
0.4~0.8 |
0.80~1.2 |
<0.70 |
0.15~0.4 |
<0.15 |
<0.25 |
0.04~0.35 |
<0.15 |
| 6082 |
0.7~1.3 |
0.60~1.2 |
<0.50 |
<0.1 |
0.4~1.0 |
<0.20 |
<0.25 |
<0.10 |
| 6351 |
0.7~1.3 |
0.40~0.8 |
<0.50 |
<0.1 |
0.4~0.8 |
<0.20 |
~ |
<0.10 |
2) Mechanical property
| Alloy |
Temper |
Tensile strength |
Yield strength |
Elongation |
|
6063
|
T5 |
≥ 160Mpa |
≥ 110Mpa |
≥ 8% |
| T6 |
≥ 205Mpa |
≥ 180Mpa |
≥ 8% |
| 6061 |
T5 |
≥ 265Mpa |
≥ 245Mpa |
≥ 8%
|