Customized Champagne Aluminium Window Frames Frame With Alloy 6063-T5
Detailed Product Description
|
Product Name: |
Aluminium |
Alloy: |
6063,6060,6463 |
|
|
|
|
Anodizing |
|
Deep Process : |
Milling, Drilling ,Bending, Cutting |
Temper: |
T5,T6,T66 |
Primary Technical Data
1) Chemical composition
|
Alloy |
Si |
Mg |
Fe |
Cu |
Mn |
Zn |
Cr |
Ti |
|
6063 |
0.2~0.6 |
0.45~0.90 |
<0.35 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
|
6060 |
0.3~0.6 |
0.35~0.60 |
0.1~0.3 |
~ |
<0.10 |
<0.15 |
<0.05 |
~ |
|
6463 |
0.2~0.6 |
0.45~0.90 |
<0.15 |
<0.20 |
<0.05 |
<0.05 |
~ |
~ |
|
6005 |
0.6~0.9 |
0.40~0.60 |
<0.35 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
<0.10 |
|
6061 |
0.4~0.8 |
0.80~1.2 |
<0.70 |
0.15~0.4 |
<0.15 |
<0.25 |
0.04~0.35 |
<0.15 |
|
6082 |
0.7~1.3 |
0.60~1.2 |
<0.50 |
<0.1 |
0.4~1.0 |
<0.20 |
<0.25 |
<0.10 |
|
6351 |
0.7~1.3 |
0.40~0.8 |
<0.50 |
<0.1 |
0.4~0.8 |
<0.20 |
~ |
<0.10 |
2) Mechanical property
|
Alloy |
Temper |
Tensile strength |
Yield strength |
Elongation |
|
6063 |
T5 |
≥ 160Mpa |
≥ 110Mpa |
≥ 8% |
|
T6 |
≥ 205Mpa |
≥ 180Mpa |
≥ 8% |
|
|
6061 |
T5 |
≥ 265Mpa |
≥ 245Mpa |
≥ 8% |
Packaging & Shipping
|
Packaging Details: |
1. Plastic film or cartons, then on pallet; |
|
Delivery Detail: |
Within 25 working days after received advanced payment |
Equipment
|
Production lines |
Quantity |
Max product length |
|
Extrusion press |
26 press range from 500MT to 2500MT |
Circumcircle diameter≤2200mm |
|
Anodizing and electrophoresis |
3 |
≤7500mm |
|
Powder Coating |
2 |
≤8500mm |
|
Wood Grain |
1 |
≤8500mm |
|
Painting |
1 |
≤8500mm |
|
Polishing |
1 |
≤6000mm |
|
Brushing |
1 |
≤6000mm |
Advantages of the extrusion process :
The extrusion process provides virtually unlimited opportunities for aluminium product shapes. Costs are cut by designing fewer components, which reduce fabrication and simplify assembly.
These features and benefits are unmatched by other materials and processes:
(1) Complex integral shapes
(2) Cost effective
(3) Low tooling costs
(4) Design flexibility
(5) Versatility in joining
(6) Machinable
(7) Rapid prototyping
(8) Short lead times
(9) Wide range of finishes